Continuous Electrical Conductivity Variation in M3(Hexaiminotriphenylene)2(M = Co, Ni, Cu) MOF Alloys · Chen T., Dou J.-H., Yang L. et al. · Journal of the American Chemical Society · 2020 · 12367-12373
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Co3(HITP)2 powder/pellet · Powder
TA Instruments Q500; 2.0 C/min under air flow 5 mL/min from room temperature to 600 C.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| pronounced weight loss onset | above 200 C | — | — | Caption Approximate | S20 · Section S6 · Figure S12 |
Cu3(HITP)2 powder/pellet · Powder
TA Instruments Q500; 2.0 C/min under air flow 5 mL/min from room temperature to 600 C.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| pronounced weight loss onset | above 200 C | — | — | Caption Approximate | S20 · Section S6 · Figure S12 |
Ni3(HITP)2 powder/pellet · Powder
TA Instruments Q500; 2.0 C/min under air flow 5 mL/min from room temperature to 600 C.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| pronounced weight loss onset | above 200 C | — | — | Caption Approximate | S20 · Section S6 · Figure S12 |