Porosity — Mixed Ionic and Electronic Conductivity in a Tetrathiafulvalene-Phosphonate Metal-Organic Framework

Measurement evidence

Porosity

Mixed Ionic and Electronic Conductivity in a Tetrathiafulvalene-Phosphonate Metal-Organic Framework · Ribeiro C., Tan B., Figueira F. et al. · Journal of the American Chemical Society · 2025 · 63-68

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Volumetric gas sorption, Micromeritics 3Flex

Gas sorption and porosity

Activated TTFTP-La MOF · Powder

Samples degassed at 150 °C under vacuum before CO2 at 273 K and N2 at 77 K measurements.

Temperature: 273 for CO2; 77 for N2
Atmosphere: CO2 or N2
Context: activated pristine framework
Measurement source: 65 · main text · Figure S23

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CO2 uptake	80 cm3 g-1 at 273 K and 1 bar	—	—	Text Rounded Reported	65 · main text · Figure S23
Pore size from distribution analysis	4.1 Å	—	—	Text Rounded Reported	65 · main text · Figure S23