Measurement evidence
Precise tuning of interlayer electronic coupling in layered conductive metal-organic frameworks · Lu Y., Zhang Y., Yang C.-Y. et al. · Nature Communications · 2022 · 7240
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Ni3(HATI_C1)2 black powder · Powder
TA Instrument Q600 under N2, 5 C/min; supercritical CO2 drying 4 h, 90 C overnight, in-situ activation 100 C for 1 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| decomposition onset | >200 C | — | — | Caption Approximate | 18 · Supplementary Figure 7 · Supplementary Fig. 7 |
| desolvation onset | >100 C | — | — | Caption Approximate | 18 · Supplementary Figure 7 · Supplementary Fig. 7 |
Ni3(HATI_C3)2 black powder · Powder
TA Instrument Q600 under N2, 5 C/min; supercritical CO2 drying 4 h, 90 C overnight, in-situ activation 100 C for 1 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| decomposition onset | >200 C | — | — | Caption Approximate | 18 · Supplementary Figure 7 · Supplementary Fig. 7 |
| desolvation onset | >100 C | — | — | Caption Approximate | 18 · Supplementary Figure 7 · Supplementary Fig. 7 |
Ni3(HATI_C4)2 black powder · Powder
TA Instrument Q600 under N2, 5 C/min; supercritical CO2 drying 4 h, 90 C overnight, in-situ activation 100 C for 1 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| decomposition onset | >200 C | — | — | Caption Approximate | 18 · Supplementary Figure 7 · Supplementary Fig. 7 |
| desolvation onset | >100 C | — | — | Caption Approximate | 18 · Supplementary Figure 7 · Supplementary Fig. 7 |