van der Pauw electrical conductivity
pressed pellet of Ni3(HITP)2 · Pellet
Measured at 25, 30, 35, 40, and 45 C in a 4-arm probe station; pellet on 300 nm SiO2/Si wafer with four gold wires and carbon paste contacts; desolvated at 150 C for 2 h, then measured in the dark under dynamic vacuum.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Electrical conductivity at 25 C | 58.8 S cm^-1 at 25 C | 5880 S m^-1 | — | Text Exact Reported | p005 / article p.171 · Results · Figure 2A |
| Electrical conductivity at 30 C | approximately 59.6 S cm^-1 at 30 C from Figure 2A | 5960 S m^-1 | error bar shown, not digitised | Figure Axis Approximate | p005 / article p.171 · Results · Figure 2A |
| Electrical conductivity at 35 C | approximately 60.5 S cm^-1 at 35 C from Figure 2A | 6050 S m^-1 | error bar shown, not digitised | Figure Axis Approximate | p005 / article p.171 · Results · Figure 2A |
| Electrical conductivity at 40 C | approximately 61.2 S cm^-1 at 40 C from Figure 2A | 6120 S m^-1 | error bar shown, not digitised | Figure Axis Approximate | p005 / article p.171 · Results · Figure 2A |
| Electrical conductivity at 45 CMarked as a best value within this paper | 62.1 S cm^-1 at 45 C | 6210 S m^-1 | — | Text Exact Reported | p005-p006 / article pp.171-172 · Results · Figure 2A |