Drawing sensors with ball-milled blends of metal-organic frameworks and graphite · Ko M., Aykanat A., Smith M.K. et al. · Sensors (Switzerland) · 2017 · 2192
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Co3HHTP2/graphite blended pellet · Pellet
TGA thermographs for MOF/graphite blend
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co3HHTP2/graphite mass loss at 600 C (first main-text statement) | 72% mass loss at 600 C | — | — | Text Rounded Reported | 6 of 17 · Results 3.2 · Figure S9 |
| Co3HHTP2/graphite mass loss at 600 C (later main-text statement) | 65% mass loss | — | — | Text Rounded Reported | 6 of 17 · Results 3.2 · Figure S9 |
pure Co3HHTP2 powder · Powder
TGA thermographs for pure MOFs; mass loss values reported at 600-750 C depending on passage
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| co3hhtp2 tga mass loss | 71% mass loss | — | — | Text Rounded Reported | 5-6 of 17 · Results 3.1-3.2 · Figure S9 |
Cu3HHTP2/graphite blended pellet · Pellet
TGA thermographs for MOF/graphite blend
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Cu3HHTP2/graphite mass loss | 31% mass loss at 600 C | — | — | Text Rounded Reported | 6 of 17 · Results 3.2 · Figure S9 |
pure Cu3HHTP2 powder · Powder
TGA thermographs for pure MOFs; mass loss values reported at 600-750 C depending on passage
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| cu3hhtp2 tga mass loss | 31% mass loss | — | — | Text Rounded Reported | 5-6 of 17 · Results 3.1-3.2 · Figure S9 |
Fe3HHTP2/graphite blended pellet · Pellet
TGA thermographs for MOF/graphite blend
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Fe3HHTP2/graphite mass loss | 59% mass loss | — | — | Text Rounded Reported | 6 of 17 · Results 3.2 · Figure S9 |
pure Fe3HHTP2 powder · Powder
TGA thermographs for pure MOFs; mass loss values reported at 600-750 C depending on passage
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| fe3hhtp2 tga mass loss | 51% mass loss | — | — | Text Rounded Reported | 5-6 of 17 · Results 3.1-3.2 · Figure S9 |
| fe3hhtp2 tga mass loss 650c | 50% mass loss at 650 C | — | — | Text Rounded Reported | 5-6 of 17 · Results 3.1-3.2 · Figure S9 |
Ni3HHTP2/graphite blended pellet · Pellet
TGA thermographs for MOF/graphite blend
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Ni3HHTP2/graphite mass loss at 600 C | 55% mass loss at 600 C | — | — | Text Rounded Reported | 6 of 17 · Results 3.2 · Figure S9 |
| Ni3HHTP2/G and Co3HHTP2/G low-temperature mass loss | 3% mass loss at 100 C | — | — | Text Rounded Reported | 6 of 17 · Results 3.2 · Figure S9 |
pure Ni3HHTP2 powder · Powder
TGA thermographs for pure MOFs; mass loss values reported at 600-750 C depending on passage
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|