Diffraction Structure — In situ construction of a dual-metal 2D conjugated metal-organic framework on carbon paper for asymmetric supercapacitors

Measurement evidence

Diffraction Structure

In situ construction of a dual-metal 2D conjugated metal-organic framework on carbon paper for asymmetric supercapacitors · Qian L., Tong Z., Jia Y. et al. · Electrochemistry Communications · 2025 · 108077

1 measurement group · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

X-ray diffraction with simulated patterns

X-ray diffraction and scattering

M1/M2-HHTP powder series · Powder

XRD patterns collected for bimetallic M1/M2-HHTP and compared with Materials Studio simulations; SI reports Bruker D8 Advance, Cu K alpha, lambda = 1.5406 A, 2theta = 3-50 degrees.

Geometry: powder
Context: pristine bimetallic c-MOF powders
Measurement source: XRD calculations · Figure 1d

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Bimetal substitution peak shift	Delta 2theta < 0.2 degrees	—	<	Text Rounded Reported	XRD calculations
XRD (002) peak	2theta = 28.0 degrees	—	—	Text Rounded Reported	2 · 3. Results and discussion · Figure 1d
XRD (020) peak	2theta = 9.4 degrees	—	—	Text Rounded Reported	2 · 3. Results and discussion · Figure 1d
XRD (100) peak	2theta = 4.7 degrees	—	—	Text Rounded Reported	2 · 3. Results and discussion · Figure 1d
XRD (210) peak	2theta = 12.6 degrees	—	—	Text Rounded Reported	2 · 3. Results and discussion · Figure 1d