Spectroscopy — Porous lanthanide metal–organic frameworks with metallic conductivity

2 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

La1.5HOTP single-crystal conductivity devices · Single Crystal

In-plane and out-of-plane oriented La1.5HOTP and Nd1.5HOTP crystals on 500 um Z-cut quartz substrates

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Absorption maximum orthogonal to c direction	around 2.1 to 2.3 eV	—	—	Text Range	p002-p003 · Results and Discussion/Fig. 2C
Absorption maximum along c direction	below 2 eV	—	—	Text Approximate	p002-p003 · Results and Discussion/Fig. 2C

Nd1.5HOTP single crystal for diffraction/refinement · Single Crystal

In-plane and out-of-plane oriented single crystals; 0.22 mW, 10 s exposure; spectra fit with cubic spline background and Lorentzian peaks

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Raman bands showing anomalies	1,100- to 1,600-cm-1 range	—	—	Caption Range	p005 · Fig. 4 caption
Raman anomaly transition range	about 350 to 360 K	—	—	Caption Range	p005 · Fig. 4 caption