Microscopy Morphology — Enhancement of Electrical Conductivity due to Structural Distortion from Linear to Nonlinear Dicarboxylato-Bridged Zn(II) 1D-Coordination Polymers

2 measurement groups · 10 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Compound 1 bulk crystals/powder · Single Crystal

JEOL JSM-6700F field-emission SEM with EDS.

Geometry: bulk crystals
Context: pristine compound 1 bulk sample
Measurement source: p007-p008; SI pages S7-S8 · FESEM and EDS elemental mapping/spectrum · Figure S6; Table S3

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
EDS C weight percent	63.79 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS N weight percent	6.89 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS O weight percent	16.44 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS S weight percent	5.52 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS Zn weight percent	7.36 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3

Compound 2 bulk crystals/powder · Single Crystal

JEOL JSM-6700F field-emission SEM with EDS.

Geometry: bulk crystals
Context: pristine compound 2 bulk sample
Measurement source: p007-p008; SI pages S7-S8 · FESEM and EDS elemental mapping/spectrum · Figure S6; Table S3

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
EDS C weight percent	60.01 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS N weight percent	0.00 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS O weight percent	23.88 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS S weight percent	3.57 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3
EDS Zn weight percent	12.54 wt%	—	—	SI Table Rounded Reported	p008; SI page S8 · Table S3 · Table S3