Diffraction Structure — Preparation of Bimetallic Conductive Metal-organic Framework Material Ni/Co-CAT for Electrocatalytic Oxygen Reduction 双金属导电金属有机框架材料 Ni/Co-CAT 的制备及其氧还原催化性能研究

Measurement evidence

Diffraction Structure

Preparation of Bimetallic Conductive Metal-organic Framework Material Ni/Co-CAT for Electrocatalytic Oxygen Reduction 双金属导电金属有机框架材料 Ni/Co-CAT 的制备及其氧还原催化性能研究 · Geng Y., Lin X., Sun Y. et al. · Acta Chimica Sinica · 2022 · 748-755

1 measurement group · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

powder XRD

X-ray diffraction and scattering

Ni-Co-CAT powder · Powder

Bruker TTR3, Cu Kα radiation (λ = 0.15418 nm), 40 kV, 40 mA.

Context: pristine Ni-CAT and Ni-Co-CAT powders
Measurement source: 749, 754 · 2.1; 4.5 · Figure 2a

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
XRD diffraction peak	9.5 degrees 2θ	—	—	Text Rounded Reported	749 · 2.1 · Figure 2a
XRD diffraction peak	14.2 degrees 2θ	—	—	Text Rounded Reported	749 · 2.1 · Figure 2a
XRD diffraction peak	16.5 degrees 2θ	—	—	Text Rounded Reported	749 · 2.1 · Figure 2a