Porosity — Near IR Bandgap Semiconducting 2D Conjugated Metal-Organic Framework with Rhombic Lattice and High Mobility

Measurement evidence

Porosity

Near IR Bandgap Semiconducting 2D Conjugated Metal-Organic Framework with Rhombic Lattice and High Mobility · Sporrer L., Zhou G., Wang M. et al. · Angewandte Chemie - International Edition · 2023 · e202300186

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 adsorption, BET analysis

Gas sorption and porosity

Cu2(OHPTP) bulk powder · Powder

Nitrogen adsorption measurements at 77 K on QuadraSorb low-pressure system.

Temperature: 77
Atmosphere: N2
Context: pristine framework porosity
Measurement source: 4 · Results and Discussion · Figure 1c

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface areaMarked as a best value within this paper	741 m2 g-1	741 m2 g-1	—	Text Exact Reported	4 · Results and Discussion · Figure 1c
average pore sizeMarked as a best value within this paper	about 1.23 nm	1.23 nm	—	Text Approximate	4 · Results and Discussion · Figure 1c