Microscopy Morphology — Synthesis, characterisation and thermal degradation behaviour of some coordination polymers by using TG-DTG and DTA techniques

4 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Co(II)-fbpmpc coordination polymer powder · Powder

SEM at 20 kV; article states magnification x5000 in text, while figure panels display x1500.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
fibre diameter	90 nm	—	—	Text Exact Reported	p006 · 3.2. Morphological behaviour · Figure 4b

Cu(II)-fbpmpc coordination polymer powder · Powder

SEM at 20 kV; article states magnification x5000 in text, while figure panels display x1500.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
fine tentacle size	100 nm	—	—	Text Exact Reported	p007 · 3.2. Morphological behaviour · Figure 4d
large tentacle diameter	935.22 nm	—	—	Text Exact Reported	p006 · 3.2. Morphological behaviour · Figure 4d

Mn(II)-fbpmpc coordination polymer powder · Powder

SEM at 20 kV; article states magnification x5000 in text, while figure panels display x1500.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
large bead diameter	851.53 nm	—	—	Text Exact Reported	p006 · 3.2. Morphological behaviour · Figure 4a
small bead size	80 nm	—	—	Text Exact Reported	p006 · 3.2. Morphological behaviour · Figure 4a

Ni(II)-fbpmpc coordination polymer powder · Powder

SEM at 20 kV; article states magnification x5000 in text, while figure panels display x1500.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
SEM morphology	unclear image; small irregular particles entrapped in larger particles forming cotton-like structure	—	—	Text Qualitative	p006 · 3.2. Morphological behaviour · Figure 4c