cMOF Evidence Base
Other — Conductive 2D metal-organic framework for high-performance cathodes in aqueous rechargeable zinc batteries

Measurement evidence

Other

Conductive 2D metal-organic framework for high-performance cathodes in aqueous rechargeable zinc batteries · Nam K.W., Park S.S., dos Reis R. et al. · Nature Communications · 2019 · 4948

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

thermogravimetric analysis (TGA)

Thermogravimetric analysis

fully discharged Cu3(HHTP)2 electrode · Electrode

Temperature raised from room temperature to 300 deg C at 5 deg C min^-1 under Ar flow.

Atmosphere
Ar
Context
pristine and discharged composite electrodes
Measurement source
rendered pages 4 and 8 / article pp.4 and 8 · Origin of high rate performance; Methods - Characterization · Supplementary Fig. 8
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
discharged electrode H2O content / weight lossMarked as a best value within this paper26.9% weight loss between 120 and 300 deg C——Text
Exact Reported		rendered page 4 / article p.4 · Origin of high rate performance · Supplementary Fig. 8
pristine electrode H2O content / weight loss8.43%——Figure Axis
Exact Reported		rendered page 11 / response p.9 · Reviewer response, added Supplementary Fig. 11 · Added Supplementary Fig. 11 / final Supplementary Fig. 8