powder X-ray diffraction with Rietveld refinement
Cu-HHTP dried powder · Powder
Rigaku Miniflex II, Cu K alpha; experimental and simulated PXRD compared with AA/AB stacking models.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Rietveld axial microstrain | 55.2k microstrain | — | — | Visual Estimate Approximate | p002 · Results and Discussion · Figure 1a inset |
| Rietveld crystallite size | 124.8 nm | — | — | Visual Estimate Approximate | p002 · Results and Discussion · Figure 1a inset |
| Rietveld equatorial microstrain | 49.8k microstrain | — | — | Visual Estimate Approximate | p002 · Results and Discussion · Figure 1a inset |
| interlayer distance from (002) stacking | about 3.2 Angstrom | — | — | Text Approximate | p002 · Results and Discussion · Figure 1 |
| common PXRD peak | near 4.7 deg 2theta | — | — | Text Approximate | p002 · Results and Discussion · Figure 1 |
| common PXRD peak | near 9.5 deg 2theta | — | — | Text Approximate | p002 · Results and Discussion · Figure 1 |
| common PXRD peak | near 12.6 deg 2theta | — | — | Text Approximate | p002 · Results and Discussion · Figure 1 |