Measurement evidence
Why conductivity is not always king-physical properties governing the capacitance of 2D metal-organic framework-based EDLC supercapacitor electrodes: A Ni3(HITP)2case study · Borysiewicz M.A., Dou J.-H., Stassen I. et al. · Faraday Discussions · 2021 · 298-304
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
HITP_A Ni3(HITP)2 powder batch · Powder
N2 adsorption at 77 K; BET fit shown in SI Fig. S2.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | 260 m2 g^-1 | — | — | Table Rounded Reported | main p.2, article p.299 · Main text · Table 1 |
HITP_B Ni3(HITP)2 powder batch · Powder
N2 adsorption at 77 K; BET fit shown in SI Fig. S3.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface areaMarked as a best value within this paper | 825 m2 g^-1 | — | — | Table Rounded Reported | main p.2, article p.299 · Main text · Table 1 |
HITP_C Ni3(HITP)2 powder batch · Powder
N2 adsorption at 77 K; BET fit shown in SI Fig. S4.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | 585 m2 g^-1 | — | — | Table Rounded Reported | main p.2, article p.299 · Main text · Table 1 |