Diffraction Structure — Synthesis of Tostadas-Shaped Metal-Organic Frameworks for Remitting Capacity Fading of Li-Ion Batteries

Measurement evidence

Diffraction Structure

Synthesis of Tostadas-Shaped Metal-Organic Frameworks for Remitting Capacity Fading of Li-Ion Batteries · Cai Y., Wang W., Cao X. et al. · Advanced Functional Materials · 2022 · 2109927

1 measurement group · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

powder X-ray diffraction (Cu Kalpha)

X-ray diffraction and scattering

NHM; Tostadas-shaped Ni-HITP assembly · Powder

As-synthesised NHP, NHM, and NHS; 2theta 4-40 deg; 2 deg min-1 in SI method.

Geometry
powder diffraction
Context
pristine Ni-HITP samples
Measurement source
p002 · Results and Discussion · Figure 1a
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
XRD peak in-plane peak12.6 deg 2theta——Text
Exact Reported		p002 · Results and Discussion · Figure 1a
XRD peak in-plane peak16.5 deg 2theta——Text
Exact Reported		p002 · Results and Discussion · Figure 1a
XRD peak broad (001)27.3 deg 2theta——Text
Exact Reported		p002 · Results and Discussion · Figure 1a
XRD peak (100)4.7 deg 2theta——Text
Exact Reported		p002 · Results and Discussion · Figure 1a
XRD peak (200)9.5 deg 2theta——Text
Exact Reported		p002 · Results and Discussion · Figure 1a