Measurement evidence
Quantum Effects Allow the Construction of Two-Dimensional Co3O4-Embedded Nitrogen-Doped Porous Carbon Nanosheet Arrays from Bimetallic MOFs as Bifunctional Oxygen Electrocatalysts · Zhang H., Xu J., Jin Y. et al. · Chemistry - A European Journal · 2018 · 14522-14530
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Co3O4-NC-n-m series · Powder
XRD patterns of ZnCo-ZIF-derived products calcined at 900 C.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Co3O4 product XRD peak positions | 2theta = 19, 31.3, 36.9, 44.8, 59.4, and 65.2 degrees | — | — | Text Rounded Reported | 14524-14525 · Results and Discussion · Figure 2b |
ZnCo-ZIF-15 precursor · Powder
XRD patterns of ZnCo-ZIF-5, ZnCo-ZIF-10, and ZnCo-ZIF-15 precursors; measurement row anchored to ZnCo-ZIF-15 series endpoint.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| FWHM at 12.8 degrees for ZnCo-ZIF-5/10/15 | 0.25, 0.33, 0.41 degrees | — | — | Text Rounded Reported | 14524 · Results and Discussion · Figure 2a |
| FWHM at 18.1 degrees for ZnCo-ZIF-5/10/15 | 0.25, 0.36, 0.41 degrees | — | — | Text Rounded Reported | 14524 · Results and Discussion · Figure 2a |
| FWHM at 7.4 degrees for ZnCo-ZIF-5/10/15 | 0.31, 0.36, 0.47 degrees | — | — | Text Rounded Reported | 14524 · Results and Discussion · Figure 2a |
| Strongest three ZnCo-ZIF XRD peak positions | 7.4, 12.8, and 18.1 degrees 2theta | — | — | Text Rounded Reported | 14524 · Results and Discussion · Figure 2a |
| ZnCo-ZIF XRD phase assignment | diffraction peaks match simulated ZIF-67/ZIF-8 | — | — | Text Qualitative | 14523 · Results and Discussion · Figure 2a |