cMOF Evidence Base
Electrical Transport — Fibrous Pb(II)-Based Coordination Polymer Operable as a Photocatalyst and Electrocatalyst for High-Rate, Selective CO2-to-Formate Conversion

Measurement evidence

Electrical Transport

Fibrous Pb(II)-Based Coordination Polymer Operable as a Photocatalyst and Electrocatalyst for High-Rate, Selective CO2-to-Formate Conversion · Suppaso C., Nakazato R., Nakahata S. et al. · Advanced Functional Materials · 2025 · 2417223

1 measurement group · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Time-resolved microwave conductivity (TRMC), 355 nm Nd:YAG excitation

Electrical conductivity

MW_x KGF-9/KGF-17 comparison powder series · Powder

Sample on adhesive tape; 5-8 ns pulse, 10 Hz, I0 = 9.1e15 photons cm-2 pulse-1, microwave frequency ca. 9 GHz, power ca. 3 mW.

Geometry
powder adhered to adhesive tape
Context
Photoconductivity comparison of ordinary and MW-derived KGF-9 powders.
Measurement source
9 · Experimental Section
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
TRMC phi Sigma mu maximum, MW_1209.9 x 10^-5 cm2 V-1 s-1——Figure Axis
Rounded Reported		4 · 2.2 Photocatalytic CO2 Reduction Activity · Figure 2B
TRMC phi Sigma mu maximum, MW_6010.1 x 10^-5 cm2 V-1 s-1——Figure Axis
Rounded Reported		4 · 2.2 Photocatalytic CO2 Reduction Activity · Figure 2B
TRMC phi Sigma mu maximum, MW_90Marked as a best value within this paper11.2 x 10^-5 cm2 V-1 s-1——Figure Axis
Rounded Reported		4 · 2.2 Photocatalytic CO2 Reduction Activity · Figure 2B
TRMC phi Sigma mu maximum, ordinary KGF-95.1 x 10^-5 cm2 V-1 s-1——Figure Axis
Rounded Reported		4 · 2.2 Photocatalytic CO2 Reduction Activity · Figure 2B