Electrical Transport — Two one-dimensional germanium(IV) coordination polymers based on macrocyclic tetraaza[14]annulene with notable semiconducting property

2 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

pressed-pellet powder compaction of compound 1 · Pellet

Pressed-pellet powder compaction measured from 200 to 300 K; Fig. 4 plots conductivity versus temperature.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
low-temperature electrical conductivity of compound 1	approximately 2 x 10^-11 S cm^-1 at 200 K from Fig. 4	2e-9 S m^-1	—	Figure Axis Approximate	4 · Figure · Fig. 4
room-temperature electrical conductivity of compound 1	1.52 x 10^-8 S cm^-1 at 293 K	0.00000152 S m^-1	—	Text Exact Reported	2 · Conductivity discussion · Fig. 4
semiconductor-like temperature coefficient	conductivity increases with increasing temperature	—	—	Text Qualitative	2 · Conductivity discussion · Fig. 4

pressed-pellet powder compaction of compound 2 · Pellet

Pressed-pellet powder compaction measured from 200 to 300 K; Fig. 4 plots conductivity versus temperature.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
low-temperature electrical conductivity of compound 2	approximately 1 x 10^-8 S cm^-1 at 200 K from Fig. 4	0.000001 S m^-1	—	Figure Axis Approximate	4 · Figure · Fig. 4
room-temperature electrical conductivity of compound 2Marked as a best value within this paper	1.18 x 10^-5 S cm^-1 at 293 K	0.00118 S m^-1	—	Text Exact Reported	2 · Conductivity discussion · Fig. 4
semiconductor-like temperature coefficient for compound 2	conductivity increases with increasing temperature from 200 to 300 K	—	—	Text Qualitative	2 · Conductivity discussion · Fig. 4