Porosity — Toward High-Performance Metal–Organic-Framework-Based Quasi-Solid-State Electrolytes: Tunable Structures and Electrochemical Properties

4 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

HKUST-1 nanoparticles · Powder

Degassed MOFs at 150 C for 12 h before measurement.

Temperature: 77
Geometry: powder adsorption
Context: pristine MOF host
Measurement source: SI p.S-30 · N2 adsorption-desorption isotherms · Table S3

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	373 m2 g-1	—	—	SI Table Exact Reported	SI p.S-30 · N2 physisorption · Table S3
pore size range	0.80-25.25 nm	—	—	SI Table Range	SI p.S-30 · N2 physisorption · Table S3
cumulative pore volume	0.63 cm3 g-1	—	—	SI Table Exact Reported	SI p.S-30 · N2 physisorption · Table S3

Mg-MOF-74 hollow nanoparticle aggregates · Powder

Degassed MOFs at 150 C for 12 h before measurement.

Temperature: 77
Geometry: powder adsorption
Context: pristine MOF host
Measurement source: SI p.S-79 · N2 adsorption-desorption isotherms · Table S10

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	1623 m2 g-1	—	—	SI Table Exact Reported	SI p.S-79 · N2 physisorption · Table S10
pore size range	0.86-27.27 nm	—	—	SI Table Range	SI p.S-79 · N2 physisorption · Table S10
cumulative pore volume	0.65 cm3 g-1	—	—	SI Table Exact Reported	SI p.S-79 · N2 physisorption · Table S10

MOF-5 nanoparticles · Powder

Degassed MOFs at 150 C for 12 h before measurement.

Temperature: 77
Geometry: powder adsorption
Context: pristine MOF host
Measurement source: SI p.S-30 · N2 adsorption-desorption isotherms · Table S3

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	720 m2 g-1	—	—	SI Table Exact Reported	SI p.S-30 · N2 physisorption · Table S3
pore size range	0.50-27.27 nm	—	—	SI Table Range	SI p.S-30 · N2 physisorption · Table S3
cumulative pore volume	0.26 cm3 g-1	—	—	SI Table Exact Reported	SI p.S-30 · N2 physisorption · Table S3

Zn-MOF-74 activated nanoparticles · Powder

Degassed MOFs at 150 C for 12 h before measurement.

Temperature: 77
Geometry: powder adsorption
Context: pristine MOF host
Measurement source: SI p.S-30 · N2 adsorption-desorption isotherms · Table S3

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	882 m2 g-1	—	—	SI Table Exact Reported	SI p.S-30 · N2 physisorption · Table S3
pore size range	0.80-27.27 nm	—	—	SI Table Range	SI p.S-30 · N2 physisorption · Table S3
cumulative pore volume	0.65 cm3 g-1	—	—	SI Table Exact Reported	SI p.S-30 · N2 physisorption · Table S3