High performance Li-, Na-, and K-ion storage in electrically conducting coordination polymers · Wang J., Guo X., Apostol P. et al. · Energy and Environmental Science · 2022 · 3923-3932

2 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Apparent powder density measurement

pristine A2-TM-PTtSA powder set · Powder

Measured apparent density of A2-TM-PTtSA CP powders.

Context: pristine powders
Measurement source: p003 / article p.3925 · Results and discussion

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
A2-TM-PTtSA apparent powder density range	1.6-2.0 g cm^-3	—	—	Text Range	p003 / article p.3925 · Results and discussion

Elemental analysis by CHNS combustion, F ion chromatography, and ICP-OES metals analysis

Bulk elemental and compositional analysis

pristine A2-TM-PTtSA powder set · Powder

Combined CHNSO and ICP-OES elemental analysis of pristine A2-TM-PTtSA CP powders.

Context: pristine powders
Measurement source: p006 / SI p.6 · Materials characterizations · Figure S5

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Li2-Co-PTtSA found Co content	Co found 10.23 wt%	—	—	Figure Axis Approximate	p014 / SI p.14 · Figure S5 · Figure S5
Li2-Co-PTtSA found Li content	Li found 2.60 wt%	—	—	Figure Axis Approximate	p014 / SI p.14 · Figure S5 · Figure S5