Measurement evidence
Copper-Metal Organic Frameworks Electrodeposited on Carbon Paper as an Enhanced Cathode for the Hydrogen Evolution Reaction · Li X.-F., Lu M.-Y., Yu H.-Y. et al. · ChemElectroChem · 2019 · 4507-4510
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
HKUST-1 ED on carbon paper · Electrode
CV in 0.425-0.625 V vs RHE at different scan rates; current density plotted against scan rate to estimate Cdl.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Double-layer capacitance CdlMarked as a best value within this paper | 0.26 mF cm^-2 | — | — | Text Exact Reported | 4509 · Results · Figure 3c |
HKUST-1 HT drop-cast electrode · Electrode
CV in 0.425-0.625 V vs RHE at different scan rates; current density plotted against scan rate to estimate Cdl.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Double-layer capacitance Cdl | 0.19 mF cm^-2 | — | — | Text Exact Reported | 4509 · Results · Figure 3c |
HKUST-1 ED on carbon paper · Electrode
HER stability in acid media at fixed voltage corresponding to 10 mA cm^-2 over 12 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| HER durability over 12 hMarked as a best value within this paper | relative current density kept well during 12 h continuous operation | — | — | Text Qualitative | 4509 · Results · Figure 3d |
HKUST-1 HT drop-cast electrode · Electrode
HER stability in acid media at fixed voltage corresponding to 10 mA cm^-2 over 12 h.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| HER durability over 12 h | decreased to 70% | — | — | Text Exact Reported | 4509 · Results · Figure 3d |
Pure carbon paper · Electrode
Pure carbon paper control in 0.5 M H2SO4; scan rate 1 mV s^-1 for HER polarisation.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Tafel slope | 279.3 mV dec^-1 | — | — | Text Exact Reported | 4509 · Results · Figure 3b |
HKUST-1 ED on carbon paper · Electrode
0.5 M H2SO4, scan rate 1 mV s^-1; three-electrode system; N2 bubbled for 30 min; potentials converted to RHE.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| HER onset potentialMarked as a best value within this paper | about -400 mV (vs. RHE) | — | about | Text Approximate | 4508 · Results · Figure 3a |
| HER overpotential at -10 mA cm^-2Marked as a best value within this paper | about -590 mV (vs. RHE) at -10 mA cm^-2 | — | about | Text Approximate | 4508 · Results · Figure 3a |
| Tafel slopeMarked as a best value within this paper | 183.6 mV dec^-1 | — | — | Text Exact Reported | 4509 · Results · Figure 3b |
HKUST-1 HT drop-cast electrode · Electrode
0.5 M H2SO4, scan rate 1 mV s^-1; three-electrode system; N2 bubbled for 30 min; potentials converted to RHE.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| HER onset potential | about -490 mV (vs. RHE) | — | about | Text Approximate | 4509 · Results · Figure 3a |
| HER overpotential at -10 mA cm^-2 | about -660 mV (vs. RHE) at -10 mA cm^-2 | — | about | Text Approximate | 4509 · Results · Figure 3a |
| Tafel slope | 222.4 mV dec^-1 in main text; 222.48 mV dec^-1 in Table S2 | — | — | SI Table Exact Reported | SI p009 · Table S2 · Table S2 |