Measurement evidence
Design and synthesis of hydroxide ion-conductive metal-organic frameworks based on salt inclusion · Sadakiyo M., Kasai H., Kato K. et al. · Journal of the American Chemical Society · 2014 · 1702-1705
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
NBu4-ZIF-8 powder · Powder
Nitrogen flow 100 ml/min; heating rate 5 C/min; RT to 900 C.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Salt inclusion state stability | stable up to 120 C | — | — | Text Rounded Reported | 1703 · Thermal analysis · Figures S3-S4 |
| NBu4-ZIF-8 weight-loss event temperature | weight loss at 127 C | — | — | Text Exact Reported | 1703 · Thermal analysis · Figure S3 |
NBu4-ZIF-8 powder · Powder
Helium flow 30 ml/min; heating rate 3 C/min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| TPD-MS desorbed species mass 18 | M = 18 (H2O) | — | — | Caption Exact Reported | S5 · Figure S4 · Figure S4 |
| TPD-MS desorbed species mass 44 | M = 44 (CO2) | — | — | Caption Exact Reported | S5 · Figure S4 · Figure S4 |
| TPD-MS desorbed species mass 56 | M = 56 (C4H8) | — | — | Caption Exact Reported | S5 · Figure S4 · Figure S4 |