Measurement evidence
Superexchange Charge Transport in Loaded Metal Organic Frameworks · Neumann T., Liu J., Wachter T. et al. · ACS Nano · 2016 · 7085-7093
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
F4-TCNQ-loaded HKUST-1 SURMOF, 5 spray cycles · Thin Film
Representative 5 spray-cycle F4-TCNQ-loaded SURMOF compared with pristine film.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Framework crystallinity after F4-TCNQ loading | no change in SURMOF orientation or crystallinity | — | — | Text Qualitative | 7089 · Results and Discussion · Figure 4b |
Pristine HKUST-1 SURMOF, 5 spray cycles · Thin Film
Bruker D8 Advance theta-theta geometry, Cu K alpha radiation, 5-25 degree 2theta, 0.024 degree step, 16.4 s per step.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| HKUST-1 SURMOF (111) Bragg peak | 2theta = 5.83 degrees | — | — | Text Exact Reported | 7089 · Results and Discussion · Figure 4a,b |
| HKUST-1 SURMOF (222) Bragg peak | 2theta = 11.68 degrees | — | — | Text Exact Reported | 7089 · Results and Discussion · Figure 4a,b |
| HKUST-1 SURMOF (333) Bragg peak | 2theta = 17.58 degrees | — | — | Text Exact Reported | 7089 · Results and Discussion · Figure 4a,b |
| HKUST-1 SURMOF high-angle Bragg peak | 2theta = 23.56 degrees | — | — | Text Exact Reported | 7089 · Results and Discussion · Figure 4a,b |
TCNQ-loaded HKUST-1 SURMOF, 5 spray cycles · Thin Film
Representative 5 spray-cycle TCNQ-loaded SURMOF compared with pristine film.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Framework crystallinity after TCNQ loading | no change in SURMOF orientation or crystallinity | — | — | Text Qualitative | 7089 · Results and Discussion · Figure 4a |