cMOF Evidence Base
Porosity — Conductive Metal–Organic Frameworks with Extra Metallic Sites as an Efficient Electrocatalyst for the Hydrogen Evolution Reaction

Measurement evidence

Porosity

Conductive Metal–Organic Frameworks with Extra Metallic Sites as an Efficient Electrocatalyst for the Hydrogen Evolution Reaction · Huang H., Zhao Y., Bai Y. et al. · Advanced Science · 2020 · 2000012

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 adsorption/desorption pore-size distribution

Gas sorption and porosity

Ni3(Ni3.HAHATN)2 nanosheets · Nanosheet

Nitrogen sorption performed after degassing Ni3(Ni3.HAHATN)2 at 150 C for 10 h.

Atmosphere
Nitrogen sorption; degassed before testing
Context
pristine Ni3(Ni3.HAHATN)2 nanosheets
Measurement source
main p.3 and p.8, article p.2000012-3 and 8 · Results and Discussion; Experimental Section · Figure S6
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
Pore-size distribution broad peak46.3 nm——Text
Exact Reported		main p.3, article p.2000012-3 · Results and Discussion · Figure S6
Pore-size distribution small peakabout 2.6 nm—aboutText
Approximate		main p.3, article p.2000012-3 · Results and Discussion · Figure S6