Other — Metal-Organic Framework Glass Catalysts from Melting Glass-Forming Cobalt-Based Zeolitic Imidazolate Framework for Boosting Photoelectrochemical Water Oxidation

2 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

10% Co-agZIF-62 glass · Powder

Zn and Co ratios of mechanochemically produced ZIF-62 crystal and glass samples

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Co content in 10% Co-agZIF-62	Co (%) = 9.94	—	—	SI Table Exact Reported	26 · Supporting Information · Table S1
Zn content in 10% Co-agZIF-62	Zn (%) = 90.06	—	—	SI Table Exact Reported	26 · Supporting Information · Table S1
Co content in 10% Co-ZIF-62 crystal	Co (%) = 9.61	—	—	SI Table Exact Reported	26 · Supporting Information · Table S1

10% Co-agZIF-62 glass · Powder

10 C min-1 heating rate under N2; repeated DSC up-scans for glass transition

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
10% Co-agZIF-62 glass transition temperature	320.8 C	593.95 K	—	Text Exact Reported	4 · Results and Discussion · Figure 1e
10% Co-ZIF-62 melting temperature	369.3 C	642.45 K	—	Text Exact Reported	4 · Results and Discussion · Figure 1d
10% Co-ZIF-62 thermal stability	stable up to about 550 C	823.15 K	about	Text Approximate	4 · Results and Discussion · Figure 1c