Porosity — Metal-Organic Framework Glass Catalysts from Melting Glass-Forming Cobalt-Based Zeolitic Imidazolate Framework for Boosting Photoelectrochemical Water Oxidation

Measurement evidence

Porosity

Metal-Organic Framework Glass Catalysts from Melting Glass-Forming Cobalt-Based Zeolitic Imidazolate Framework for Boosting Photoelectrochemical Water Oxidation · Song Y., Ren Y., Cheng H. et al. · Angewandte Chemie - International Edition · 2023 · e202306420

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

CO2 adsorption-desorption isotherms; BET analysis

Gas sorption and porosity

10% Co-agZIF-62 glass · Powder

Measured at 298 K

Temperature: 298
Atmosphere: CO2
Context: MOF precursor versus glass
Measurement source: 4 · Results and Discussion · Figure 1f

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
CO2 adsorption capacity retained after melt-quench	Co-agZIF-62 still retains high microporosity and CO2 adsorption capacity	—	—	Text Qualitative	4 · Results and Discussion · Figure 1f