Electrical Transport — 2D Rhodium-Isocyanide Frameworks

3 measurement groups · 13 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

as-prepared SJTU-201 powder · Powder

dry N2-purged environment at room temperature; 800 nm Ti:sapphire laser; frequency-resolved photoconductivity globally fitted

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
dc-limit mobility	17 +/- 1 cm2 V-1 s-1	—	+/- 1	SI Table Exact Reported	92 · Supplementary Tables · Table S4
intrinsic electron-hole sum mobilityMarked as a best value within this paper	560 +/- 46 cm2 V-1 s-1	—	+/- 46	SI Table Exact Reported	92 · Supplementary Tables · Table S4
effective mass used in TRTS fit	0.154m0	—	—	SI Table Exact Reported	92 · Supplementary Tables · Table S4

as-prepared SJTU-202 powder · Powder

dry N2-purged environment at room temperature; 800 nm Ti:sapphire laser; frequency-resolved photoconductivity globally fitted

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
dc-limit mobility	9 +/- 1 cm2 V-1 s-1	—	+/- 1	SI Table Exact Reported	92 · Supplementary Tables · Table S4
intrinsic electron-hole sum mobility	312 +/- 25 cm2 V-1 s-1	—	+/- 25	SI Table Exact Reported	92 · Supplementary Tables · Table S4
effective mass used in TRTS fit	0.276m0	—	—	SI Table Exact Reported	92 · Supplementary Tables · Table S4
global Drude-Smith backscattering parameter	-0.97 +/- 0.02	—	+/- 0.02	SI Table Exact Reported	92 · Supplementary Tables · Table S4
photoconductivity decay time	about 2 ps	—	—	Text Approximate	8 · TRTS · Figure 5h
photoconductivity rise time	within 1 ps	—	—	Text Approximate	8 · TRTS · Figure 5h
global Drude-Smith scattering time	49 +/- 4 fs	—	+/- 4	SI Table Exact Reported	92 · Supplementary Tables · Table S4

as-prepared SJTU-203 powder · Powder

dry N2-purged environment at room temperature; 800 nm Ti:sapphire laser; frequency-resolved photoconductivity globally fitted

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
dc-limit mobility	13 +/- 1 cm2 V-1 s-1	—	+/- 1	SI Table Exact Reported	92 · Supplementary Tables · Table S4
intrinsic electron-hole sum mobility	418 +/- 34 cm2 V-1 s-1	—	+/- 34	SI Table Exact Reported	92 · Supplementary Tables · Table S4
effective mass used in TRTS fit	0.206m0	—	—	SI Table Exact Reported	92 · Supplementary Tables · Table S4