Microscopy Morphology — In Situ Growth of Lithiophilic MOF Layer Enabling Dendrite-free Lithium Deposition

3 measurement groups · 6 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Li@Cu-MOF-30 min · Electrode

Cu, Cu-MOF-30 min and Cu-MOF-24 h after 10 cycles at Li stripping state and after 100 cycles at Li plating state.

Geometry: SEM
Context: Li@Cu-MOF electrodes compared with Li@Cu
Measurement source: p021 / SI p.9 · Supplemental Figure S4 caption · Figure S4A-F

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Li@Cu-MOF-30 min morphology after 100 cycles at Li plating stateMarked as a best value within this paper	Compact surface composed of large-sized Li particles without dendritic Li	—	—	Text Qualitative	p008 / journal p.7 · Morphology Evolution · Figure S4E

Cu-MOF-30 min · Electrode

Initial surface morphology of Cu-MOF-30 min, Cu-MOF-24 h and Cu foil before Li deposition.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Cu-MOF-24 h initial morphology	Cu-MOF particles accumulate at some sites, resulting in an uneven surface	—	—	Text Qualitative	p003 / journal p.2 · Synthesis and Characterization · Figure 2B
Cu-MOF-30 min initial morphologyMarked as a best value within this paper	Thin layer of nanosized Cu-MOF particles homogeneously covers Cu foil	—	—	Text Qualitative	p003 / journal p.2 · Synthesis and Characterization · Figure 2A

Cu-MOF-30 min · Electrode

Cu, Cu-MOF-30 min and Cu-MOF-24 h after deposition of 2.0 mAh cm^-2 Li at 0.5 mA cm^-2.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Li deposition morphology on Cu foil	Uneven Li deposition with clear emergence of dendrite	—	—	Text Qualitative	p004 / journal p.3 · Synthesis and Characterization · Figures 2F and 2I
Li deposition morphology on Cu-MOF-24 h	Non-uniform Li deposition with some exposed Cu-MOF-24 h; no dendrite observed	—	—	Text Qualitative	p004 / journal p.3 · Synthesis and Characterization · Figures 2E and 2H
Li deposition morphology on Cu-MOF-30 minMarked as a best value within this paper	Uniform Li deposition without dendrite formation; no gaps in cross-section	—	—	Text Qualitative	p004 / journal p.3 · Synthesis and Characterization · Figures 2D and 2G