Measurement evidence
Two dimensional Conjugated Metal–Organic Frameworks with Multiple Redox-Active Sites towards High-Performance Sodium-Ion Battery · Qi M., Cheng L., Zhang X. et al. · Advanced Science · 2025 · 2503369
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Cu-DDQP black powder · Powder
PXRD experimental/refined/calculated patterns in Figure 2b.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Pawley Rp | Rp = 2.57% | — | — | Figure Axis Rounded Reported | 4 · Results · Figure 2b |
| Pawley Rwp | Rwp = 3.39% | — | — | Figure Axis Rounded Reported | 4 · Results · Figure 2b |
| AA stacking d-spacing | 3.21 A | — | — | Text Rounded Reported | 4 · Results · Figure 1b-d |
Cu-TBPQ black powder · Powder
PXRD experimental/refined/calculated patterns in Figure 2a.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Pawley Rp | Rp = 5.29% | — | — | Figure Axis Rounded Reported | 4 · Results · Figure 2a |
| Pawley Rwp | Rwp = 7.71% | — | — | Figure Axis Rounded Reported | 4 · Results · Figure 2a |
| AA stacking d-spacing | 3.49 A | — | — | Text Rounded Reported | 4 · Results · Figure 1b-d |
Cu-TTPQ black powder · Powder
PXRD compared with simulated stacking models; Cu target tube.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Pawley cell a | a = 19.22 A | — | — | Text Rounded Reported | 4 · Results · Figure 2c |
| Pawley cell b | b = 19.21 A | — | — | Text Rounded Reported | 4 · Results · Figure 2c |
| Pawley cell c | c = 3.16 A | — | — | Text Rounded Reported | 4 · Results · Figure 2c |
| Pawley gamma angle | gamma = 111.2 deg | — | — | Text Rounded Reported | 4 · Results · Figure 2c |
| Pawley Rp | Rp = 2.61% | — | — | Text Exact Reported | 4 · Results · Figure 2c |
| Pawley Rwp | Rwp = 3.42% | — | — | Text Exact Reported | 4 · Results · Figure 2c |
Cu-TTPQ black powder · Powder
Cu-TTPQ immersed in H2O, THF, acetone, DMF, 1 M AcOH and 1 M NaOH for five days; PXRD after exposure.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Solvent stability | PXRD retained after five days in H2O, THF, acetone, DMF, 1 M AcOH and 1 M NaOH | — | — | Qualitative Qualitative | S22 · Section 11 · Figure S20 |