Electrical Transport — Two dimensional Conjugated Metal–Organic Frameworks with Multiple Redox-Active Sites towards High-Performance Sodium-Ion Battery

3 measurement groups · 9 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Cu-DDQP pellet for two-probe conductivity · Pellet

Keithley 4200-SCS source meter; voltage sweep -1.0 to 1.0 V at room temperature.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
electrical conductivity	2.3e-06 S cm-1	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2
pellet resistance	186.92 KOhm	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2
pellet thickness	0.343 mm	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2

Cu-TBPQ pellet for two-probe conductivity · Pellet

Keithley 4200-SCS source meter; voltage sweep -1.0 to 1.0 V at room temperature.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
electrical conductivity	6.1e-07 S cm-1	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2
pellet resistance	952.39 KOhm	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2
pellet thickness	0.296 mm	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2

Cu-TTPQ pellet for two-probe conductivity · Pellet

Keithley 4200-SCS source meter; voltage sweep -1.0 to 1.0 V at room temperature.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
electrical conductivityMarked as a best value within this paper	5.6e-06 S cm-1	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2
pellet resistance	61.35 KOhm	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2
pellet thickness	0.266 mm	—	—	SI Table Exact Reported	S25 · Section 14 · Table S2