Measurement evidence
Two dimensional Conjugated Metal–Organic Frameworks with Multiple Redox-Active Sites towards High-Performance Sodium-Ion Battery · Qi M., Cheng L., Zhang X. et al. · Advanced Science · 2025 · 2503369
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Cu-DDQP black powder · Powder
N2 sorption at 77 K after activation at 80 deg C for 12 h under vacuum (10^-5 bar).
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | S_BET = 339 m2 g-1 | — | — | Figure Axis Rounded Reported | S24 · Section 13 · Figure S22c |
| dominant pore size | 1.38 nm | — | — | Figure Axis Rounded Reported | S24 · Section 13 · Figure S22d |
Cu-TBPQ black powder · Powder
N2 sorption at 77 K after activation at 80 deg C for 12 h under vacuum (10^-5 bar).
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | S_BET = 357 m2 g-1 | — | — | Figure Axis Rounded Reported | S24 · Section 13 · Figure S22a |
| dominant pore size | 1.37 nm | — | — | Figure Axis Rounded Reported | S24 · Section 13 · Figure S22b |
Cu-TTPQ black powder · Powder
N2 sorption at 77 K after activation at 80 deg C for 12 h under vacuum (10^-5 bar).
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface area | S_BET = 321 m2 g-1 | — | — | Figure Axis Rounded Reported | S24 · Section 13 · Figure S22e |
| dominant pore size | 1.41 nm | — | — | Figure Axis Rounded Reported | S24 · Section 13 · Figure S22f |