Electrical Transport — Flexible conductive metal-organic framework Cu3(HHTP)2 film with high thermoelectric performance for low-grade heat harvesting

Measurement evidence

Electrical Transport

Flexible conductive metal-organic framework Cu3(HHTP)2 film with high thermoelectric performance for low-grade heat harvesting · Wu X., Zheng Q., Sun T. et al. · Journal of Alloys and Compounds · 2025 · 183333

1 measurement group · 5 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Cyclic bending test with electrical-conductivity retention

Electrical conductivity

Optimised Cu3(HHTP)2/Nylon bending-test film · Thin Film

Film strips bent around a 6 mm diameter rod; conductivity ratio sigma/sigma0 tracked with bending cycles.

Temperature: room temperature
Geometry: 20 x 10 mm strip; 6 mm rod diameter, equivalent to 3 mm bending radius.
Context: target composite hot-pressed film
Measurement source: main p.5-7 · 3. Results and discussion · Figure 5a

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
bending-cycle count	650 bending cycles	—	—	Text Exact Reported	main p.5 · 3. Results and discussion · Figure 5a
bending radius	3 mm bending radius	0.003 m	—	Text Exact Reported	main p.1,p.5 · Abstract; 3. Results and discussion · Figure 5a
electrical-conductivity retention after bendingMarked as a best value within this paper	about 75% of initial electrical conductivity retained after 650 bending cycles	0.75 fraction of initial conductivity	—	Text Approximate	main p.1,p.5 · Abstract; 3. Results and discussion · Figure 5a
bending-test strip length	20 mm	0.02 m	—	Text Exact Reported	main p.5 · 3. Results and discussion · Figure 5
bending-test strip width	10 mm	0.01 m	—	Text Exact Reported	main p.5 · 3. Results and discussion · Figure 5