Measurement evidence
Solid state electrical conductivity studies on manganese-molybdenum Schiff base polymer · Suganya S., Xavier F.P., Nagaraja K.S. · Bulletin of Materials Science · 1998 · 403-407
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
dark yellow manganese-molybdenum Schiff base polymer solid · Powder
Powder form at room temperature
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| EPR metal-centre assignment | no Mo(V) signal; ill-defined fine-line pattern due to Mn(II); interpreted as Mn(II) and Mo(VI) | — | — | Text Qualitative | 406 · 4. Results and discussion |
dark yellow manganese-molybdenum Schiff base polymer solid · Powder
4000-40 cm^-1 spectral range
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| azomethine C=N IR band | 1610 cm^-1 | — | — | Text Rounded Reported | 406 · 4. Results and discussion · Figure 3 |
| phenolic oxygen IR band | 1100 cm^-1 | — | — | Text Rounded Reported | 406 · 4. Results and discussion · Figure 3 |
| weak trans dioxo molybdenum band | 900 cm^-1 | — | — | Text Rounded Reported | 406 · 4. Results and discussion · Figure 3 |
dark yellow manganese-molybdenum Schiff base polymer solid · Powder
1H NMR spectrum of coordination polymer
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| 1H NMR coordination assignment | supports coordination of azomethine nitrogen and aromatic structure | — | — | Text Qualitative | 406 · 4. Results and discussion · Figure 4 |