Electrochemistry Application — Dye-sensitized solar cells with new one-dimensional halide-bridged Cu(I)-Ni(II) heterometal coordination polymers containing hexamethylene dithiocarbamate ligand

5 measurement groups · 20 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

DSSC with 1a/TiO2 photoelectrode · Electrode

AM 1.5 G irradiation, 100 mW/cm2; Bunkoukeiki KP-3201 solar simulator; device area 0.30 cm2.

Atmosphere: not specified
Geometry: sandwich DSSC; 50 um spacer; ITO/TiO2-polymer photoelectrode and PEDOT-TMA counter-electrode
Context: composite DSSC using 1a coordination-polymer sensitizer mixed with TiO2
Measurement source: p009 (journal p1621) · 3.4 · Figure 6; Table 1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
fill factor FF	0.387	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
short-circuit current density Jsc	0.171 mA/cm (table header; current density context)	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
power conversion efficiency PCE	0.034 %	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
open-circuit voltage Voc	0.519 V	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1

DSSC with 1b/TiO2 photoelectrode · Electrode

AM 1.5 G irradiation, 100 mW/cm2; Bunkoukeiki KP-3201 solar simulator; device area 0.30 cm2.

Atmosphere: not specified
Geometry: sandwich DSSC; 50 um spacer; ITO/TiO2-polymer photoelectrode and PEDOT-TMA counter-electrode
Context: composite DSSC using 1b coordination-polymer sensitizer mixed with TiO2
Measurement source: p009 (journal p1621) · 3.4 · Figure 6; Table 1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
fill factor FF	0.489	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
short-circuit current density Jsc	0.163 mA/cm (table header; current density context)	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
power conversion efficiency PCE	0.041 %	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
open-circuit voltage Voc	0.527 V	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1

DSSC with 2a/TiO2 photoelectrode · Electrode

AM 1.5 G irradiation, 100 mW/cm2; Bunkoukeiki KP-3201 solar simulator; device area 0.30 cm2.

Atmosphere: not specified
Geometry: sandwich DSSC; 50 um spacer; ITO/TiO2-polymer photoelectrode and PEDOT-TMA counter-electrode
Context: composite DSSC using 2a coordination-polymer sensitizer mixed with TiO2
Measurement source: p009 (journal p1621) · 3.4 · Figure 6; Table 1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
fill factor FF	0.492	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
short-circuit current density Jsc	0.663 mA/cm (table header; current density context)	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
power conversion efficiency PCE	0.149 %	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
open-circuit voltage Voc	0.457 V	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1

DSSC with 2b/TiO2 photoelectrode · Electrode

AM 1.5 G irradiation, 100 mW/cm2; Bunkoukeiki KP-3201 solar simulator; device area 0.30 cm2.

Atmosphere: not specified
Geometry: sandwich DSSC; 50 um spacer; ITO/TiO2-polymer photoelectrode and PEDOT-TMA counter-electrode
Context: composite DSSC using 2b coordination-polymer sensitizer mixed with TiO2
Measurement source: p009 (journal p1621) · 3.4 · Figure 6; Table 1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
fill factor FF	0.519	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
short-circuit current density Jsc	0.633 mA/cm (table header; current density context)	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
power conversion efficiency PCEMarked as a best value within this paper	0.151 %	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
open-circuit voltage Voc	0.460 V	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1

DSSC with 3/TiO2 photoelectrode · Electrode

AM 1.5 G irradiation, 100 mW/cm2; Bunkoukeiki KP-3201 solar simulator; device area 0.30 cm2.

Atmosphere: not specified
Geometry: sandwich DSSC; 50 um spacer; ITO/TiO2-polymer photoelectrode and PEDOT-TMA counter-electrode
Context: composite DSSC using 3 coordination-polymer sensitizer mixed with TiO2
Measurement source: p009 (journal p1621) · 3.4 · Figure 6; Table 1

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
fill factor FF	0.492	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
short-circuit current density Jsc	0.177 mA/cm (table header; current density context)	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
power conversion efficiency PCE	0.041 %	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1
open-circuit voltage Voc	0.478 V	—	—	Table Exact Reported	p009 (journal p1621) · 3.4 · Table 1