Microscopy Morphology — Highly Conducting Neutral Coordination Polymer with Infinite Two-Dimensional Silver-Sulfur Networks

Measurement evidence

Microscopy Morphology

Highly Conducting Neutral Coordination Polymer with Infinite Two-Dimensional Silver-Sulfur Networks · Huang X., Li H., Tu Z. et al. · Journal of the American Chemical Society · 2018 · 15153-15156

1 measurement group · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

SEM, TEM, HR-TEM, STEM, TEM-EDS

Scanning electron microscopy Transmission electron microscopy Elemental microanalysis and mapping

Ag-BHT nanocrystals exfoliated from film · Unknown

TEM with JEOL 2100F at 120 kV; high-resolution STEM with aberration-corrected Nion Ultra STEM 100 at 60 kV, ADF detector half-angle 86-200 mrad.

Context: pristine Ag-BHT film/nanocrystals
Measurement source: p001-p002 / 15153-15154 · Results and discussion · Figure 1; Figure 2c,d

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
HR-TEM lattice fringe d-spacing	3.4 A	—	—	Text Rounded Reported	p002 / 15154 · Results and discussion · Figure 1d
HR-TEM lattice fringe d-spacing	7.5 A	—	—	Text Rounded Reported	p002 / 15154 · Results and discussion · Figure 1d
nanocrystal length	1 um	—	—	Text Rounded Reported	p002 / 15154 · Results and discussion · Figure 1c
nanocrystal width	approximately 100 nm	—	—	Text Approximate	p002 / 15154 · Results and discussion · Figure 1c