Diffraction Structure — Two-Dimensional Conjugated Metal–Organic Frameworks with a Ring-in-Ring Topology and High Electrical Conductance

3 measurement groups · 13 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Co-DHHBTN powder · Powder

Rigaku Cu Kalpha and synchrotron PXRD; simulated patterns by Materials Studio Reflex Plus.

Context: powder pristine
Measurement source: 2 · Structural Characterizations · Figure 2; Figures S7-S8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Pawley cell a=b	a=b=30.15 A	—	—	Text Exact Reported	2 · Structural Characterizations · Figure 2b
Pawley cell c	c=3.43 A	—	—	Text Exact Reported	2 · Structural Characterizations · Figure 2b
PXRD in-plane peak positions	2theta = 3.3, 5.8, 8.8, 10.0, 12.1 deg for (100), (110), (210), (300), (310)	—	—	Text Rounded Reported	2 · Structural Characterizations · Figure 2a

Cu-DHHBTN powder · Powder

Rigaku Cu Kalpha and synchrotron PXRD; simulated patterns by Materials Studio Reflex Plus.

Context: powder pristine
Measurement source: 2 · Structural Characterizations · Figure 2; Figures S7-S8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Pawley cell a	a=29.73 A	—	—	Text Exact Reported	2 · Structural Characterizations · Figure 2b
Pawley cell b	b=30.04 A	—	—	Text Exact Reported	2 · Structural Characterizations · Figure 2b
Pawley cell c	c=3.47 A	—	—	Text Exact Reported	2 · Structural Characterizations · Figure 2b
PXRD in-plane peak positions	2theta = 3.6, 6.2, 9.0, 10.5, 12.5 deg	—	—	Text Rounded Reported	2 · Structural Characterizations · Figure 2a
Schematic large pore diameter	18.9 A	—	—	Figure Axis Approximate	3 · Scheme 1 · Scheme 1
Schematic rectangular pore width	10.7 A	—	—	Figure Axis Approximate	3 · Scheme 1 · Scheme 1
Schematic small pore width	6.7 A	—	—	Figure Axis Approximate	3 · Scheme 1 · Scheme 1

Ni-DHHBTN powder · Powder

Rigaku Cu Kalpha and synchrotron PXRD; simulated patterns by Materials Studio Reflex Plus.

Context: powder pristine
Measurement source: 2 · Structural Characterizations · Figure 2; Figures S7-S8

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Pawley cell a=b	a=b=30.21 A	—	—	Text Exact Reported	2 · Structural Characterizations · Figure 2b
Pawley cell c	c=3.43 A	—	—	Text Exact Reported	2 · Structural Characterizations · Figure 2b
PXRD in-plane peak positions	2theta = 3.3, 5.8, 8.8, 10.0, 12.1 deg for (100), (110), (210), (300), (310)	—	—	Text Rounded Reported	2 · Structural Characterizations · Figure 2a