N2 adsorption/desorption isotherms and BET analysis
as-synthesised Cu3HHAE2 powder/hexagonal rods · Powder
N2 sorption at 77 K / 77.3 K; powder treated in supercritical CO2 dryer 4 h and activated at 90 deg C overnight / under dynamic vacuum.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface areaMarked as a best value within this paper | 801 m2 g-1 | — | — | Text Exact Reported | 2 · Porosity · Figure 1c |
| hexagonal channel/pore diameter | about 2.2 nm | — | about | Text Approximate | 3 · Structure characterisation · Figure 2 |
| average pore size from N2 isotherm fitting | 2.16 nm | — | — | Text Exact Reported | 2 · Porosity · Figure 1c |
| triangular pore diameter | 0.3 nm | — | — | Text Rounded Reported | 3 · Structure characterisation · Figure 2 |