Microscopy Morphology — Framework Dimensional Control Boosting Charge Storage in Conjugated Coordination Polymers

Measurement evidence

Microscopy Morphology

Framework Dimensional Control Boosting Charge Storage in Conjugated Coordination Polymers · Fan K., Fu C., Chen Y. et al. · Advanced Science · 2023 · 2205760

2 measurement groups · 4 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

SEM, TEM, HRTEM

Scanning electron microscopyTransmission electron microscopy

as-synthesised 1D-CuTABQ powder · Powder

Gemini 300 SEM and JEOL 2100 TEM; HRTEM lattice fringe analysis

Geometry
powder particles
Context
pristine
Measurement source
2,5 · 2.1 Synthesis and Characterization · Figure 2; Figure S1
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
HRTEM d-spacingabout 4.75 A——Text
Approximate		5 · 2.1 Synthesis and Characterization · Figure 2b
rod length rangea few nanometers to 100 nm——Text
Range		2 · 2.1 Synthesis and Characterization · Figure 2a; Figure S1

SEM, TEM, HRTEM

Scanning electron microscopyTransmission electron microscopy

as-synthesised 2D-CuTABQ powder · Powder

Gemini 300 SEM and JEOL 2100 TEM; HRTEM lattice fringe analysis

Geometry
powder particles
Context
pristine
Measurement source
2,5 · 2.1 Synthesis and Characterization · Figure 2; Figure S2
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
HRTEM lattice fringe0.32 nm——Text
Rounded Reported		5 · 2.1 Synthesis and Characterization · Figure 2d
morphologysheet morphology——Text
Qualitative		2 · 2.1 Synthesis and Characterization · Figure 2c; Figure S2