Sensing Application — Macrocycle-Based Metal-Organic Frameworks with NO2-Driven On/Off Switch of Conductivity

Measurement evidence

Sensing Application

Macrocycle-Based Metal-Organic Frameworks with NO2-Driven On/Off Switch of Conductivity · Ma Y.-X., Gao B., Li Y. et al. · ACS Applied Materials and Interfaces · 2021 · 27066-27073

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Resistance response to N2, O2, and CO2

MOF A-100 heated/dehydrated crystals · Single Crystal

Resistance monitored during N2, O2, and CO2 introduction for about 9 min at 298 K and 1 bar.

Temperature: 298
Atmosphere: N2, O2, CO2, each at 1 bar
Geometry: resistance curve/device not fully specified
Context: activated A-100 selectivity control
Measurement source: main p.5 · Results and Discussion · Figure S25

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Resistance after N2/O2/CO2 exposure	about 5.7 × 10^11 Ω after N2, O2, and CO2 for about 9 min	—	about	Text Approximate	main p.5 · Results and Discussion · Figure S25