Powder X-ray diffraction with Pawley refinement
bulk HAN-Cu-MOF powder · Powder
Cu Kalpha irradiation; AA stacking model; P6/MMM space group
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| interlayer distance from (001) | approximately 3.3 A | — | — | Text Approximate | 6755 · Results and Discussion · Figure 1b |
| Pawley lattice parameter a | a = b = 29.71 A | — | — | Text Exact Reported | 6755 · Results and Discussion · Figure 1b,c |
| Pawley lattice parameter c | c = 3.32 A | — | — | Text Exact Reported | 6755 · Results and Discussion · Figure 1b,c |
| Pawley refinement Rp | Rp = 2.88% | — | — | Text Exact Reported | 6755 · Results and Discussion · Figure 1b |
| Pawley refinement Rwp | Rwp = 3.65% | — | — | Text Exact Reported | 6755 · Results and Discussion · Figure 1b |
| PXRD (001) peak | 27.3 deg | — | — | Text Exact Reported | 6755 · Results and Discussion · Figure 1b |
| PXRD (100) peak | 3.46 deg | — | — | Text Exact Reported | 6755 · Results and Discussion · Figure 1b |