Inductively coupled plasma-atomic emission spectroscopy (ICP-AES)
CuCo-THQ powder · Nanosheet
ICP-AES used to determine elemental composition after Cu substitution by transition metals.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Cu weight percent in Cu-THQ | 18.7 wt% | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Co weight percent in CuCo-THQ | 4.5 wt% | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Cu:Co molar ratio in CuCo-THQ | Cu:Co = 2.84 | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Cu weight percent in CuCo-THQ | 13.8 wt% | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Cu:Fe molar ratio in CuFe-THQ | Cu:Fe = 3.03 | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Cu weight percent in CuFe-THQ | 14.1 wt% | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Fe weight percent in CuFe-THQ | 4.1 wt% | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Cu:Ni molar ratio in CuNi-THQ | Cu:Ni = 3.15 | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Cu weight percent in CuNi-THQ | 14.3 wt% | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |
| Ni weight percent in CuNi-THQ | 4.2 wt% | — | — | SI Table Exact Reported | S32 / S34 · 4. Supplementary Tables · Table S1 |