Other — Conjugated Nonplanar Copper-Catecholate Conductive Metal-Organic Frameworks via Contorted Hexabenzocoronene Ligands for Electrical Conduction

3 measurement groups · 3 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

c-HBC-12O-Cu black powder · Powder

30-800 deg C, 10 deg C min-1, N2 atmosphere, empty Al2O3 crucible reference.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Weight loss at 473 K	~9.0%	—	~	Text Approximate	p004 / article p8982 · Results and Discussion · Figure S19

c-HBC-6O-Cu black powder · Powder

30-800 deg C, 10 deg C min-1, N2 atmosphere, empty Al2O3 crucible reference.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Weight loss at 473 K	~10%	—	~	Text Approximate	p004 / article p8982 · Results and Discussion · Figure S19

c-HBC-8O-Cu black powder · Powder

30-800 deg C, 10 deg C min-1, N2 atmosphere, empty Al2O3 crucible reference.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Weight loss at 473 K	9.6%	—	—	Text Exact Reported	p004 / article p8982 · Results and Discussion · Figure S19