Measurement evidence
Diverse π-π Stacking motifs modulate electrical conductivity in tetrathiafulvalene-based metal-organic frameworks · Xie L.S., Alexandrov E.V., Skorupskii G. et al. · Chemical Science · 2019 · 8558-8565
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
As-synthesised bulk powder of compound 1 · Powder
Powder samples heated between 25 and 700 deg C at 3 deg C/min under N2 flow of 35 mL/min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| TGA curve availability | TGA plot reported; no numerical decomposition temperature text-reported | — | — | Caption Qualitative | S23 · TGA · Fig. S10 |
As-synthesised bulk powder of compound 2 · Powder
Powder samples heated between 25 and 700 deg C at 3 deg C/min under N2 flow of 35 mL/min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| TGA curve availability | TGA plot reported; no numerical decomposition temperature text-reported | — | — | Caption Qualitative | S23 · TGA · Fig. S10 |
As-synthesised bulk powder of compound 3 · Powder
Powder samples heated between 25 and 700 deg C at 3 deg C/min under N2 flow of 35 mL/min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| TGA curve availability | TGA plot reported; no numerical decomposition temperature text-reported | — | — | Caption Qualitative | S23 · TGA · Fig. S10 |