Other — Giant Enhancement of Carrier Mobility in Bimetallic Coordination Polymers

Measurement evidence

Other

Giant Enhancement of Carrier Mobility in Bimetallic Coordination Polymers · Dhara B., Kumar V., Gupta K. et al. · ACS Omega · 2017 · 4488-4493

1 measurement group · 1 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

M-H and chi-T magnetic measurements using MPMS XL SQUID

Magnetometry and magnetic susceptibility

Fe-BTC-Cr 1:1 xerogel pressed pellet · Pellet

M-H plots recorded at 300 K; chi-T plots measured at 100 Oe.

Temperature
300
Geometry
powder sample
Context
pristine CPs
Measurement source
p004 · Supporting Information · Figure S6
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
magnetic behaviour of CP samplesmonometallic and bimetallic CPs were paramagnetic in nature——Text
Qualitative		p004 · Results and Discussion · Figure S6