Measurement evidence
Giant Enhancement of Carrier Mobility in Bimetallic Coordination Polymers · Dhara B., Kumar V., Gupta K. et al. · ACS Omega · 2017 · 4488-4493
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Cr-BTC xerogel pressed pellet · Pellet
N2 gas adsorption-desorption isotherm recorded at 77 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| N2 uptake near P/P0 = 1 | approximately 120 mL/g near P/P0 = 1 from Figure 3 | — | visual estimate | Figure Axis Approximate | p002 · Results and Discussion · Figure 3 |
Fe-BTC xerogel pressed pellet · Pellet
N2 gas adsorption-desorption isotherm recorded at 77 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| N2 uptake near P/P0 = 1 | approximately 80 mL/g near P/P0 = 1 from Figure 3 | — | visual estimate | Figure Axis Approximate | p002 · Results and Discussion · Figure 3 |
Fe-BTC-Cr 1:1 xerogel pressed pellet · Pellet
N2 gas adsorption-desorption isotherms recorded at 77 K.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| BET surface areaMarked as a best value within this paper | ~338 m2/g | — | — | Text Approximate | p002 · Results and Discussion · Figure 3; Table S2 |
| N2 uptake near P/P0 = 1 | approximately 400-460 mL/g near P/P0 = 1 from Figure 3 | — | visual range ~400-460 mL/g | Figure Axis Approximate | p002 · Results and Discussion · Figure 3 |