Electrical Transport — Charge Transfer-Induced Molecular Hole Doping into Thin Film of Metal-Organic Frameworks

4 measurement groups · 16 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

Iodine-doped Co3(NDC)3 doctor-blade film on glass · Thin Film

Iodine-doped Co3(NDC)3 doctor-blade film on glass measured at 25 deg C.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Iodine-doped DB film bulk carrier concentration	5.12 x 10^11 cm^-3	—	—	SI Table Exact Reported	S5 · Table S1 · Table S1
Iodine-doped DB film Hall coefficient	1.22 x 10^7 m2 C^-1	—	—	SI Table Exact Reported	S5 · Table S1 · Table S1
Iodine-doped DB film conductivity	1.02 x 10^-7 S cm^-1	1.02e-7 S cm^-1	—	SI Table Exact Reported	S5 · Table S1 · Table S1
Iodine-doped DB film mobility	1.24 cm2/Vs	—	—	SI Table Exact Reported	S5 · Table S1 · Table S1
Iodine-doped DB film resistivity	9.82 x 10^6 ohm cm	—	—	SI Table Exact Reported	S5 · Table S1 · Table S1
Iodine-doped DB film sheet carrier concentration	5.12 x 10^7 cm^-2	—	—	SI Table Exact Reported	S5 · Table S1 · Table S1

Iodine-doped Co3(NDC)3 LbL film on glass · Thin Film

Iodine-doped Co3(NDC)3 LbL film on glass measured at 25 deg C.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Iodine-doped LbL film bulk carrier concentrationMarked as a best value within this paper	5.48 x 10^11 cm^-3	—	—	Table Exact Reported	18503 · Results and Discussion · Table 1
Iodine-doped LbL film Hall coefficientMarked as a best value within this paper	1.14 x 10^7 m2 C^-1	—	—	Table Exact Reported	18503 · Results and Discussion · Table 1
Iodine-doped LbL film conductivityMarked as a best value within this paper	1.88 x 10^-6 S cm^-1	0.00000188 S cm^-1	—	Table Exact Reported	18503 · Results and Discussion · Table 1
Iodine-doped LbL film mobilityMarked as a best value within this paper	21.2 cm2/(V s)	—	—	Table Exact Reported	18503 · Results and Discussion · Table 1
Iodine-doped LbL film resistivity	5.37 x 10^5 ohm cm	—	—	Table Exact Reported	18503 · Results and Discussion · Table 1
Iodine-doped LbL film sheet carrier concentration	1.64 x 10^7 cm^-2	—	—	Table Exact Reported	18503 · Results and Discussion · Table 1

Pristine Co3(NDC)3 doctor-blade film on glass · Thin Film

Undoped Co3(NDC)3 films tested for Hall effect; instrument displayed connection fail.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Undoped film Hall measurement status	connection fail; electrical circuit could not be established	—	—	Text Qualitative	18503 · Results and Discussion · Figure S5C

Iodine-doped Co3(NDC)3 LbL film on glass · Thin Film

MOF films on nonconducting glass with silver-paste contact points; pristine and iodine-doped DB and LbL films compared.

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
Iodine-doped doctor-blade film current density at +4 V	approximately -0.0022 mA cm-2 at +4 V from Figure 3B	-0.0022 mA cm^-2	visual estimate from rendered plot	Figure Axis Approximate	18503 · Results and Discussion · Figure 3B
Iodine-doped LbL film current density at +4 V	approximately -0.0053 mA cm-2 at +4 V from Figure 3B	-0.0053 mA cm^-2	visual estimate from rendered plot	Figure Axis Approximate	18503 · Results and Discussion · Figure 3B
Pristine film current response	As-prepared MOF films without doping show insulating behaviour	—	—	Text Qualitative	18502 · Results and Discussion · Figure 3B