Porosity — Solvent-Directed Assembly of π-Stacked 3D Metal-Organic Frameworks with Tunable Conductivity Enhanced by C60 Encapsulation

8 measurement groups · 12 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 adsorption-desorption isotherm; BET

Gas sorption and porosity

NU-4000 · Single Crystal

77 K after acetone exchange and 80 C activation

Measurement source: main p002 / journal p20900 · Synthesis and Structural Characterization · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	1155 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1
calculated accessible surface area	1250 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1

CO2 adsorption isotherm; BET

Gas sorption and porosity

NU-4001 · Single Crystal

195 K after scCO2 activation

Measurement source: main p003 / journal p20901 · Synthesis and Structural Characterization · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
calculated accessible surface area	1450 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1
BET surface area from CO2 adsorption	610 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1

CO2 adsorption isotherm; BET

Gas sorption and porosity

NU-4002 · Single Crystal

195 K after scCO2 activation

Measurement source: main p003 / journal p20901 · Synthesis and Structural Characterization · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
calculated accessible surface area	600 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1
BET surface area from CO2 adsorption	210 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1

N2 adsorption-desorption isotherm; BET

Gas sorption and porosity

NU-4003 · Single Crystal

77 K after acetone exchange and 80 C activation

Measurement source: main p002 / journal p20900 · Synthesis and Structural Characterization · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	830 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1
calculated accessible surface area	865 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1

N2 adsorption-desorption isotherm; BET

Gas sorption and porosity

NU-4003-C60-0.25 · Single Crystal

77 K; partial C60 loading after 80 C activation

Measurement source: main p007 / journal p20905 · Electrical Conductivity · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	580 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1

N2 adsorption-desorption isotherm; BET

Gas sorption and porosity

NU-4003-C60-0.36 · Single Crystal

77 K; partial C60 loading after 80 C activation

Measurement source: main p007 / journal p20905 · Electrical Conductivity · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	510 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1

N2 adsorption-desorption isotherm; BET

Gas sorption and porosity

NU-4003-C60-0.54 · Single Crystal

77 K; partial C60 loading after 80 C activation

Measurement source: main p007 / journal p20905 · Electrical Conductivity · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	350 m2/g	—	—	Text Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1

N2 adsorption-desorption isotherm; BET

Gas sorption and porosity

NU-4003-C60 · Single Crystal

77 K; full C60 loading after 80 C activation

Measurement source: main p006 / journal p20904 · Electrical Conductivity · Figure 2c / Figure S19

Property	Reported value	Normalised value	Uncertainty	Origin and quality	Source
BET surface area	nearly zero; Table 1 reports 0	—	—	Table Rounded Reported	main p002-p007 / journal p20900-p20905 · Synthesis and Structural Characterization / Electrical Conductivity · Figure 2c; Table 1