Measurement evidence
Vertical Conductive Metal–Organic Framework Single-Crystalline Nanowire Arrays for Efficient Electrocatalytic Hydrogen Evolution · Dong J., Chi K., Zhao Y. et al. · Small · 2024 · 2404808
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Ag-MOF-NWs · Single Crystal
Morphology comparison of Ag-MOF-Film, Ag-MOF-MWs and Ag-MOF-NWs formed after different reaction times.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Ag-MOF-NWs mean nanowire length | approx. 1 um | — | — | Text Approximate | 3 · Synthesis and Characterization of Materials · Figure 2c,f |
Ag-MOF-NWs powder · Powder
Ultrasonically dispersed Ag-MOF nanowires characterised for dimensions, lattice fringes, diffraction and elemental distribution.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| TEM-EDX elemental distribution | homogeneous sulfur and silver distribution | — | — | Text Qualitative | 3 · Synthesis and Characterization of Materials · Figure 3e |
| HRTEM lattice fringe assigned to (10-1) | 0.43 nm | — | — | Text Exact Reported | 3 · Synthesis and Characterization of Materials · Figure 3b |
| HRTEM lattice fringe assigned to (110) | 0.78 nm | — | — | Text Exact Reported | 3 · Synthesis and Characterization of Materials · Figure 3b |
| Ag-MOF-NWs prism diameter | of the order of 100 nm | — | — | Text Approximate | 3 · Synthesis and Characterization of Materials · Figure 3a |
| Ag-MOF-NWs TEM length | approximate length of 1 um | — | — | Text Approximate | 3 · Synthesis and Characterization of Materials · Figure 3a |
| SAED single-crystalline character | bright diffraction points aligned with simulated diffraction pattern | — | — | Text Qualitative | 3 · Synthesis and Characterization of Materials · Figure 3c,d |