Measurement evidence
Asymmetrical Substitution Manipulates Stacking Modes in 2D Conductive MOF Crystals · Liu Y., Yao H., Zhang H. et al. · Journal of the American Chemical Society · 2025 · 48127-48135
Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.
Cu3F2HHTP2 blue powder/rod crystals · Powder
N2 isotherm at 77 K after outgassing at 120 degC under dynamic vacuum until outgas rate <2 mTorr/min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Cu3F2HHTP2 BET surface area | 315 m2 g-1 | — | — | Text Rounded Reported | 4 · Results and Discussion · Figure S27 |
| Cu3F2HHTP2 BJH/KJS pore size | 1.1 nm | — | — | Caption Rounded Reported | 38 · Figure S26 · Figure S26 |
Cu3FHHTP2 blue powder/rod crystals · Powder
N2 isotherm at 77 K after outgassing at 120 degC under dynamic vacuum until outgas rate <2 mTorr/min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Cu3FHHTP2 BET surface area | 205 m2 g-1 | — | — | Text Rounded Reported | 4 · Results and Discussion · Figure S25 |
| Cu3FHHTP2 BJH/KJS pore size | 1.2 nm | — | — | Caption Rounded Reported | 36 · Figure S24 · Figure S24 |
Cu3HHTP2 powder/rod crystals · Powder
N2 isotherm at 77 K after outgassing at 120 degC under dynamic vacuum until outgas rate <2 mTorr/min.
| Property | Reported value | Normalised value | Uncertainty | Origin and quality | Source |
|---|---|---|---|---|---|
| Cu3HHTP2 BET surface areaMarked as a best value within this paper | 347.2 m2 g-1 | — | — | Text Rounded Reported | 4 · Results and Discussion |