Porosity — Electrically Conductive π-Intercalated Graphitic Metal-Organic Framework Containing Alternate π-Donor/Acceptor Stacks

Measurement evidence

Porosity

Electrically Conductive π-Intercalated Graphitic Metal-Organic Framework Containing Alternate π-Donor/Acceptor Stacks · Yadav A., Zhang S., Benavides P.A. et al. · Angewandte Chemie - International Edition · 2023 · e202303819

1 measurement group · 2 results

Reported values remain attached to the sample, method, conditions, extraction quality and source location that produced them.

N2 sorption isotherm and BET surface area

Gas sorption and porosity

iGMOF1 black powder · Powder

Activated iGMOF1 and Cu3(HATP)2 measured at 77 K using Quantachrome Autosorb iQ and automated Sieverts apparatus.

Temperature
77
Atmosphere
N2
Context
Porosity comparison used to argue HCTP is in walls rather than pore channels.
Measurement source
4 · Results and Discussion · Figure S8
PropertyReported valueNormalised valueUncertaintyOrigin and qualitySource
BET surface area of pristine Cu3(HATP)2SBET = 195 m2 g-1195 m2 g-1—Text
Exact Reported		4 · Results and Discussion · Figure S8
BET surface area of evacuated iGMOF1SBET = 154 m2 g-1154 m2 g-1—Text
Exact Reported		4 · Results and Discussion · Figure S8